Most printing materials are highly hygroscopic, which means that they easily absorb ambient moisture. Even tight factory packaged filament is not always suitable for use when removed out of the box. We should bear in mind that the purchase of the material itself is not the last step before printing.
For the 3D printing process to run properly, it is essential to prepare the filament properly. Heating the material at the appropriate temperature eliminates moisture that the filament could have absorbed.
Hygroscopicity, or filament susceptibility to absorb moisture, is an undesirable phenomenon in this case, but it occurs very often, especially among engineering materials. How does it look in practice? Water settles on the outer material layers and penetrates inwards having a direct impact on the 3D printing process and models.
The hygroscopicity of filaments causes significant problems during the printing process itself, not always visible at first glance. Even a small amount of moisture in the material can have an adverse effect on:
Get the 3D printed parts you need just in time
The heating temperature is important. That is why it is particularly important to prepare filament for 3D printing in accordance with the specific recommendations for a material and heat it at a temperature that allows for removal of all moisture. At 3DGence, before we issue recommendations, we check various possibilities to make the work of users of industrial 3D printers, 3DGence INDUSTRY F340 and 3DGence INDUSTRY 420, as easy as possible.
Łukasz Lipiec, Technical Sales Support Engineer at 3DGence
The key to obtaining the desired properties of a printed part is proper heating of the material before printing. What does this process consist in?
To remove excess moisture from material, it is necessary to place a filament spool in a suitable device to dry it. The time and temperature at which the heating operation should be carried out depends on the material used.
Most engineering materials should be heated before printing to get rid of the moisture absorbed by filament from the environment. In appropriate annealing conditions, we will observe the evaporation of moisture from material. Be careful when selecting the temperature, too high a temperature can deform filament. It is recommended to follow manufacturer’s guidelines.
Check the recommendations for some engineering materials for heating them after removing them out of the box.
PA6 material has been heated at 65°C for 24h (this temperature is to low for this material)
PA6 material has been heated at 85°C for 24h (it's proper temperature to achieve good results)
Proper preparation of materials is necessary for the proper printing process. There are several ways to dry filaments.
There are many devices on the market that are dedicated to drying materials.
At 3DGence, we use a professional Drying Oven SLW 53 laboratory dryer to heat materials before use [download technical specification]
The filament drying operation, as an indispensable part of the industrial 3D printing process, should be carried out under fully controlled and predictable conditions. Drying filaments in a cooking oven does not allow full control and may even damage the material and disrupt the entire printing process.
Get the 3D printed parts you need just in time
3DGence Drying Oven SLW 53 - laboratory dryer
Heated material chamber - 3DGence INDUSTRY F420
Yes, even if we heat up the filament before printing, during the process itself, which often lasts long, the filament can absorb ambient moisture again, if it is not properly protected. That is why, to print from engineering materials with high hygroscopic properties, we should use industrial 3D printers equipped with a heated filament chamber. A heated filament chamber maintains a high temperature and restricts access of printer’s ambient air, thus preventing material from absorbing moisture again.
According to the recommendations, ULTEM filament should be heated for 24 hours at the temperature of 120⁰C. For of this test we checked what happens to the print if we do not dry this material before the printing process. We placed unheated ULTEM in the heated filament chamber of the 3DGence INDUSTRY F420 printer and started printing.
We can see that over time, the heated chamber in the 3DGence INDUSTRY F420 printer helped to evaporate moisture from the outer coils of the material. This had a significant impact on the quality of the model, which improved with the gradual removal of water from the filament. The porosity of the printed sample also decreased over time.
Tight factory packaging does not guarantee that our material has not absorbed moisture and that it will be suitable for printing without prior preparation. Although there are no visible visual differences, only the weight measurement and the appearance of the print itself can indicate that the material has absorbed some water.
If our filament is not prepared well, during extrusion from the nozzle, we can:
The consequence is a loss of extruded material used to make the layer and pores embedded in the printout structure, which weakens the printed item.
The filament weight in the package may be close to the weight of the material left in a humid environment, indicating that the filament manufacturer does not always provide appropriate conditions during packaging.
After unpacking, the weight of the Nylon 680 [Taulman] filament was 466.5 g (after subtracting the weight of the spool). The material was left for 24 hours under average temperature conditions of 23°C and air humidity of 48%. Has the material absorbed ambient moisture? Yes, after weighing the material, it turned out that its weight increased by 0.6 g to 467.1 g. Preprocessing before printing proved necessary. The material was heated in accordance with the recommendations and placed for 8 hours in a heated printing chamber at a temperature of 70°C in the 3DGence INDUSTRY F340 machine. Heating the material reduced its mass to 464.2 g. This means that the heating process removed moisture from the filament weighing 2.9 g, which is 0.62% of the filament, as before heating.
3D printed part made with Nylon 680 Taulman, the material has not been heated before use
3D printed part made with Nylon 680 Taulman, the material has been heated at 85°C for 24 hours.
Industrial 3D printer can be a complementary machine that supports traditional manufacturing processes. Choosing a proper machine that will suit your needs is not an easy task.
If you would like to know more what industrial 3D printer will be proper for your company, you can consult with 3D printing experts:
Stay up to date with our newest collections, latest projects. Stay in touch for the latest information